exothermic and insulating sleeves
1)ISO 9000 -2001
2)Good flexbility;
3)Heat & tremble resistance;
4)oil resistance;
| Property of silicone rubber coated sleeving |
| ltem | Figure | | Elasticity | The coated film shouldn't break away glass fiber or craze after treated at the temperature of 200±5°C for 3 hours. | | Flame retardant | method B for less than 60 seconds | | Heat resistance | The coated film shouldn't break away glass fiber or craze after treated at the temperature of 200±5°C for 72 hours. | | Breakdown voltage(V) | Under normal condition | 2500 | | Under moist condition | 800 |
|
| Property of self-extinguishing sleeving |
| ltem | Figure | | Flame retardant | The lacquer film shouldn't come away and colour won't be changed at constant temperature of 250±3°C for 24 hours | | Self-extinguish | Less than 10 seconds when diameter is smaller than 3.5mmLess than 15 seconds when diameter is smaller than 4mm | | Breakdown voltage(V) | 1500 |
|
| Propetry of PVC coated sleeving |
| ltem | Figure | | Bending after heat treated | The Coated film shouldn't break away or craze after treated at the temperature of 100±2°C for 96 hours. | | Bending at low temperature | The Coated film shouldn't break away or craze after treated at the temperature of 25±1°C below zero for 96 hours. | | Test condition | Breakdown voltage(V) | | Under moist condition | 1200 |
|
| Property of acrylic resin coated sleeving |
| ltem | Figure | | Figure | Breakdown voltage(V) | | Type II | | Normal condition | ≥2500 | | Under moist condition | ≥1200 | | After enwinding | ≥1400 |
|
| Glass fiber greige braided sleeving |
| ltem | Figure | | Heat resistance | ≥400°C | | Internal diameter | Φ0.5 mm---Φ50 mm | | Wall thickness | 0.2mm --1mm |
|